- concrete restoration in accordance to DIN EN 1504-3
- high-performance fine-grain concrete with soft plastic thixotropic consistence as matrix for the combination with textile fabrics TUDALIT®
- chloride-free, shrinkage-free through controller swelling
TF10 Tudalit-fine-grain concrete
portland-cement-based, fine-grain concrete, quartz sands 0-1 mm, adjusted to the TUDALIT® textile fabrics
- granularity: 0-1 mm
- layer thickness: 3-30 mm
- consumption: 1,90 kg/(m²⋅mm)
- swelling degree: +0,1 %
- processing time at 20°C (68 °F): about 60 min
- pressure resistance after 28 d: ≥ 80 N/mm²
properties
- fine-grained concrete, specially suitable for the TUDALIT® textile fabric
- soft plastic, thixotropic consistence
- controlled swelling
- low Young's modulus and high flexural strength
- low water/cement ratio
- impermeable to water and to great extent resistant against mineral oils and fuel
- pumpable and easy to process with mono-feed-pumps with regulation device (please, ask us about the suitability of your particular machine)
fields of application
- fine-grain, high-performance concrete, as matrix for textile fabric
- constructive reinforcement in the tensile area of reinforced concrete parts
- reduction of layer-thickness of concrete structures in civil engineering works (manufacture of construction parts and elements)
- reduction of layer thickness in constructive repair works
- for strengthening of reinforced steel parts both hand-spread and with the MAWO-PAGEL® dense-flow wet-spraying method